[问答]

MEMS麦克风制造的推荐焊接参数（即焊膏厚度）是多少？

问答对人有帮助，内容完整，我也想知道答案 0 MEMS麦克风制造的推荐焊接参数（即焊膏厚度）是多少？以上来自于谷歌翻译以下为原文 What are the recommended soldering parameters (i.e. solder paste thickness) for MEMS microphone manufacturing? 0
2018-9-27 16:16:47　　评论淘帖0 邀请回答您可以邀请以下用户，快速回答问题 × wang21cj 该类别下有 44 个回答。邀请回答新星之火12138 该类别下有 41 个回答。邀请回答 chm5 该类别下有 39 个回答。邀请回答 hgimtk 该类别下有 33 个回答。邀请回答 HengDu 该类别下有 30 个回答。邀请回答 hwp0415229 该类别下有 28 个回答。邀请回答 jghgfdssas 该类别下有 28 个回答。邀请回答 kingnet6688 该类别下有 26 个回答。邀请回答颜刚YanG 该类别下有 26 个回答。邀请回答可口可甜该类别下有 26 个回答。邀请回答柱子图宁该类别下有 25 个回答。邀请回答 jenny042 该类别下有 25 个回答。邀请回答 kingnet9999 该类别下有 25 个回答。邀请回答 andyfly7 该类别下有 25 个回答。邀请回答麻酱该类别下有 25 个回答。邀请回答 zyh34997 该类别下有 25 个回答。邀请回答 gXDhn 该类别下有 24 个回答。邀请回答 jiangwenwen 该类别下有 24 个回答。邀请回答哼小曲该类别下有 24 个回答。邀请回答云汉007 该类别下有 24 个回答。邀请回答举报黄明光相关推荐 • 【TI SimpleLink SensorTag试用体验】9.MEMS数位麦克风SPH0641LU 5058 • MEMS麦克风的主要声学参数是什么？他们是如何定义的？ 7349 • MEMS麦克风的声学设计方案分享 3564 • MEMS麦克风的需求分析 3004 • 请问MEMS麦克风降噪了吗？ 438 • 模拟和数字MEMS麦克风有什么不同？ 5902 • 请问ST MEMS麦克风的RF抗扰度是多少？塑料包装如何抑制辐射干扰？ 2511 • 小型模拟MEMS麦克风能实现什么功能？ 2695 • MEMS麦克风数据中的技术规格和术语看了就知道 2170 • 评估MEMS麦克风的最佳工具或设备是什么？ 1783 1个回答

答案对人有帮助，有参考价值 0 嗨，必须严格控制焊接参数，例如模板的厚度，最终焊膏厚度和平面度以及回流期间温度变化的速度，因为它们会对麦克风结构产生危险的副作用。不同的焊膏厚度可以在麦克风焊盘和封装上产生不同的力，并且过快的温度梯度可以对器件封装产生机械应力。 •建议使用不锈钢模板 •模板厚度为75 - 100μm（2.95 - 3.94 mils），建议用于丝网印刷 •模板孔径应为矩形 •信号焊盘模板的开口应在PCB焊盘的70-90％之间（每个ST麦克风的推荐模板开口如下图所示） •可选地，为了更好地释放焊膏，孔壁应为梯形，并且角部应为圆形 •精细的IC引脚间距要求模板与PCB精确对准。在应用焊膏之前，模板和印刷电路组件应对准在25μm（1密耳）以内 •最终的焊膏厚度应能够正确清洁焊剂残留物和传感器封装与PCB之间的间隙 •填充模板开口的焊膏厚度必须尽可能均匀 •必须遵循图21中所示的回流曲线 •必须避免气相回流焊接过程，因为在蒸汽阶段，一些颗粒会进入声音入口并污染MEMS传感器 •如果可能，建议在焊接过程中用泡沫或胶带密封麦克风端口孔 •请勿使用任何超声波方法清洁PCB •应避免手动焊接，因为很难确保适当的温度梯度和温度随时间的变化有关详细信息（即焊盘图案，模板开口），请从ST网站下载应用笔记AN4211 问候，亚历山德罗以上来自于谷歌翻译以下为原文 Hi, The soldering parameters such as the thickness of the stencil, the final soldering paste thickness and planarity and the velocity of the temperature change during the reflow must be rigorously controlled since they can produce dangerous side effects on the microphone structure. A different soldering paste thickness can generate different forces on microphone pads and on the package as well as an excessively fast temperature gradient can mechanically stress the device package. â€¢ Stainless steel stencils are recommended â€¢ Stencil thickness of 75 - 100 Î¼m (2.95 - 3.94 mils) is recommended for screen printing â€¢ Stencil aperture should have a rectangular shape â€¢ The openings of the stencil for the signal pads should be between 70 - 90% of the PCB pad (The recommended stencil openings for each ST microphone are shown in the following figures) â€¢ Optionally, for better solder paste release, the aperture walls should be trapezoidal and the corners rounded â€¢ The fine IC lead pitch requires accurate alignment of the stencil to the PCB. The stencil and printed circuit assembly should be aligned to within 25 Î¼m (1 mil) prior to application of the solder paste â€¢ The final soldering paste thickness should allow for proper cleaning of flux residuals and clearance between sensor package and PCB â€¢ The soldering paste thickness, filling the stencil openings, must be as homogeneous as possible â€¢ The reflow profile depicted in Figure 21 must be followed â€¢ The vapor phase reflow soldering process must be avoided since during the vapor stage some particles can enter in the sound inlet and contaminate the MEMS sensor â€¢ If possible, sealing the microphone port hole with foam or with tape during the soldering process is recommended â€¢ Do not clean the PCB with any ultrasonic method â€¢ Manual soldering should be avoided since it is difficult to ensure the proper temperature gradient and temperature variation over time For further details (i.e. land pattern, stencil openings) please download the application note AN4211 from the ST website Regards, Alessandro

2018-9-27 16:22:32 评论举报盛方圆